The poor man's clear coat:
I've used Rustoleum spray lacquer with excellent results but after a few
days - if I don't let it cure for at least a month - I get crazing/checking
in the finish. I polish the stuff up to 2000 grit then use 3M compounds and
glaze. Looks incredible but the checking is killing me! I'm doing this on
maple with water based analine dye, deft lacquer sanding sealer (aerosol)
and my question is...if I use deft aerosol lacquer will I have better
results? I've heard that the deft is actually nitro in a can with some
solids added, and others have said they don't have the crazing problems with
it. I just wanted to fish for other opinions.
Thanks!
V
Vaughn wrote:
> > Too many coats too fast will cause prolonged drying times, but they
should
> > not cause drying times that are measured in days and even longer.
One
> > thing
> > I can assure you is that even though the schedule seems to breathe
right
> > down your neck, everytime you rush it, push it, ignore the
manufacturer's
> > advice, you end up with more time tacked on the project. Resist
the
> > temptation to rush it and follow the manufacturer's instructions.
>
> Words to live by!
Or die (dye?) beneath! 8^)
I've used Deft for many projects. It's not as durable as urethane or maybe
even other lacquers but it's *almost* idiot proof. I like it a lot.
"Vaughn" <[email protected]> wrote in message
news:[email protected]...
> The poor man's clear coat:
>
> I've used Rustoleum spray lacquer with excellent results but after a few
> days - if I don't let it cure for at least a month - I get
crazing/checking
> in the finish. I polish the stuff up to 2000 grit then use 3M compounds
and
> glaze. Looks incredible but the checking is killing me! I'm doing this
on
> maple with water based analine dye, deft lacquer sanding sealer (aerosol)
> and my question is...if I use deft aerosol lacquer will I have better
> results? I've heard that the deft is actually nitro in a can with some
> solids added, and others have said they don't have the crazing problems
with
> it. I just wanted to fish for other opinions.
>
> Thanks!
>
> V
>
>
Too many coats too fast?
--
Rumpty
Radial Arm Saw Forum: http://forums.delphiforums.com/woodbutcher/start
- - - - - - - - - - - - - - - - - - - - -
"Vaughn" <[email protected]> wrote in message
news:[email protected]...
> The poor man's clear coat:
>
> I've used Rustoleum spray lacquer with excellent results but after a few
> days - if I don't let it cure for at least a month - I get
crazing/checking
> in the finish. I polish the stuff up to 2000 grit then use 3M compounds
and
> glaze. Looks incredible but the checking is killing me! I'm doing this
on
> maple with water based analine dye, deft lacquer sanding sealer (aerosol)
> and my question is...if I use deft aerosol lacquer will I have better
> results? I've heard that the deft is actually nitro in a can with some
> solids added, and others have said they don't have the crazing problems
with
> it. I just wanted to fish for other opinions.
>
> Thanks!
>
> V
>
>
yeah, that's what I was thinking too but I have heard that the deft won't
give you that trouble with too much too fast. problem is, and I think it's
just a matter of me having to chill a bit, that I have demand to meet and
only one me to do the work and only so many hours in the evening to get the
work done. Thanks for the feedback, keep it coming pleeeze!
V
"Rumpty" <[email protected]> wrote in message
news:[email protected]...
> Too many coats too fast?
>
> --
>
> Rumpty
>
> Radial Arm Saw Forum: http://forums.delphiforums.com/woodbutcher/start
>
> - - - - - - - - - - - - - - - - - - - - -
>
>
> "Vaughn" <[email protected]> wrote in message
> news:[email protected]...
>> The poor man's clear coat:
>>
>> I've used Rustoleum spray lacquer with excellent results but after a few
>> days - if I don't let it cure for at least a month - I get
> crazing/checking
>> in the finish. I polish the stuff up to 2000 grit then use 3M compounds
> and
>> glaze. Looks incredible but the checking is killing me! I'm doing this
> on
>> maple with water based analine dye, deft lacquer sanding sealer (aerosol)
>> and my question is...if I use deft aerosol lacquer will I have better
>> results? I've heard that the deft is actually nitro in a can with some
>> solids added, and others have said they don't have the crazing problems
> with
>> it. I just wanted to fish for other opinions.
>>
>> Thanks!
>>
>> V
>>
>>
>
>
thanks, appreciate the suggestion!
"B a r r y" <[email protected]> wrote in message
news:[email protected]...
> Vaughn wrote:
>> The poor man's clear coat:
>
> H. Behlen's Lacquers work great from a spray bomb.
>
> You could also try a shellac barrier coat, like Seal Coat or Zinnser
> spray-on clear, underneath the Rustoleum.
>
> Barry
> Too many coats too fast will cause prolonged drying times, but they should
> not cause drying times that are measured in days and even longer. One
> thing
> I can assure you is that even though the schedule seems to breathe right
> down your neck, everytime you rush it, push it, ignore the manufacturer's
> advice, you end up with more time tacked on the project. Resist the
> temptation to rush it and follow the manufacturer's instructions.
Words to live by!
idiot proof? duuuuhhh, I can get behind that ;-). I shot sprayed some last
night, levels out and dries fast. pretty cool stuff.
"NorthIdahoWWer" <[email protected]> wrote in message
news:[email protected]...
> I've used Deft for many projects. It's not as durable as urethane or
> maybe
> even other lacquers but it's *almost* idiot proof. I like it a lot.
>
>
> "Vaughn" <[email protected]> wrote in message
> news:[email protected]...
>> The poor man's clear coat:
>>
>> I've used Rustoleum spray lacquer with excellent results but after a few
>> days - if I don't let it cure for at least a month - I get
> crazing/checking
>> in the finish. I polish the stuff up to 2000 grit then use 3M compounds
> and
>> glaze. Looks incredible but the checking is killing me! I'm doing this
> on
>> maple with water based analine dye, deft lacquer sanding sealer (aerosol)
>> and my question is...if I use deft aerosol lacquer will I have better
>> results? I've heard that the deft is actually nitro in a can with some
>> solids added, and others have said they don't have the crazing problems
> with
>> it. I just wanted to fish for other opinions.
>>
>> Thanks!
>>
>> V
>>
>>
>
>
"Vaughn" <[email protected]> wrote in message
news:[email protected]...
> The poor man's clear coat:
>
> I've used Rustoleum spray lacquer with excellent results but after a few
> days - if I don't let it cure for at least a month - I get
crazing/checking
> in the finish.
How can it be excellent results if the finish checks? Checking in the
finish is an indicator of reaction between the coat you spray on and
whatever is beneath it. Rustoleum in particular is well known for very slow
drying times. The finish may seem to be hard to the touch, but can still be
bleeding solvents and that will cause nothing but problems. The first thing
I would do would be to use a different product than Rustoleum. I don't use
Rustoleum for anything, and I do a lot of painting. Try Plasticoat products
or Krylon products. And... make sure you are not mixing lacquers and
enamels on your different coats. Very bad mix.
> I polish the stuff up to 2000 grit then use 3M compounds and
> glaze. Looks incredible but the checking is killing me! I'm doing this
on
> maple with water based analine dye, deft lacquer sanding sealer (aerosol)
> and my question is...if I use deft aerosol lacquer will I have better
> results? I've heard that the deft is actually nitro in a can with some
> solids added, and others have said they don't have the crazing problems
with
> it. I just wanted to fish for other opinions.
>
The best way to know this is to try it. Just to be rid of the Rustoleum
product in your process would be an accomplishment.
--
-Mike-
[email protected]
"Vaughn" <[email protected]> wrote in message
news:[email protected]...
> yeah, that's what I was thinking too but I have heard that the deft won't
> give you that trouble with too much too fast. problem is, and I think
it's
> just a matter of me having to chill a bit, that I have demand to meet and
> only one me to do the work and only so many hours in the evening to get
the
> work done. Thanks for the feedback, keep it coming pleeeze!
>
Too many coats too fast will cause prolonged drying times, but they should
not cause drying times that are measured in days and even longer. One thing
I can assure you is that even though the schedule seems to breathe right
down your neck, everytime you rush it, push it, ignore the manufacturer's
advice, you end up with more time tacked on the project. Resist the
temptation to rush it and follow the manufacturer's instructions. You'll
come out better with respect to your schedule.
--
-Mike-
[email protected]
>
> "Rumpty" <[email protected]> wrote in message
> news:[email protected]...
> > Too many coats too fast?
> >
> > --
> >
> > Rumpty
> >
> > Radial Arm Saw Forum: http://forums.delphiforums.com/woodbutcher/start
> >
> > - - - - - - - - - - - - - - - - - - - - -
> >
> >
> > "Vaughn" <[email protected]> wrote in message
> > news:[email protected]...
> >> The poor man's clear coat:
> >>
> >> I've used Rustoleum spray lacquer with excellent results but after a
few
> >> days - if I don't let it cure for at least a month - I get
> > crazing/checking
> >> in the finish. I polish the stuff up to 2000 grit then use 3M
compounds
> > and
> >> glaze. Looks incredible but the checking is killing me! I'm doing
this
> > on
> >> maple with water based analine dye, deft lacquer sanding sealer
(aerosol)
> >> and my question is...if I use deft aerosol lacquer will I have better
> >> results? I've heard that the deft is actually nitro in a can with some
> >> solids added, and others have said they don't have the crazing problems
> > with
> >> it. I just wanted to fish for other opinions.
> >>
> >> Thanks!
> >>
> >> V
> >>
> >>
> >
> >
>
>